C83600 Nodweddion:although the strength is lower than aluminum bronze (e.g., C95400) and high strength brass, it is superior to other copper alloys in wear resistance and friction reduction. Cast tin bronze surface can form dense SnO2 film, which has good protective effect, so in pump, valve water supply and drain line and Mae gan long . offer llong ystod eang o ddefnyddiau . |
||||||||||||
|
Alwai |
Rhif aloi copr uns |
Prif Gyfansoddiad Cemegol/% |
KSI [MPA] o isafswm cryfder tynnol |
Cryfder cynnyrch lleiaf KSI [MPA] |
Estyniadau o 2 fodfedd [50.08 mm],% |
|||||||
|
Gopr |
Blaeni |
Tunia ’ |
Sinc |
Alwminiwm |
Siligon |
Antimoni |
Smwddiant |
|||||
|
Efydd tun |
C83600 |
84.0---86.0 |
0.005 |
4.0---6.0 |
4.0---6.0 |
4.0---6.0 |
0.005 |
0.25 |
0.30 |
30[205] |
14[95] |
20 |
C83600 Triniaeth Gwres:triniaeth datrysiad solet (dim llai nag 1 awr ac yna diffodd dŵr)
|
Sail |
ISO o safonau rhyngwladol |
Cyn Undeb Sofietaidd |
Unol Daleithiau (Symbol) |
Japaniaid |
Yr Almaen |
Brydain |
Ffrainc |
|
Zcusn5pb5zn5 |
Cupb5sn5zn5 |
BPO5ц5C5 |
C83600 |
Bc6 |
G-CUSN5ZNPB |
Lg2 |
Cupb5sn5zn5 |
|
ZCUSN3ZN11PB4 Nodweddion:Perfformiad castio da, prosesu hawdd, ymwrthedd cyrydiad, yn bennaf yn gweithredu'n bennaf mewn dŵr y môr, dŵr croyw, stêm, pwysau dim mwy na 2 . 5 MPa o ffitiadau pibellau. |
|||||||||||
|
Enw'r Alloy |
Gradd aloi |
Prif Gyfansoddiad Cemegol/% |
Gradd aloi |
Dull castio |
Priodweddau mecanyddol, dim llai na |
||||||
|
Gopr |
Blaeni |
Tunia ’ |
Sinc |
cryfder tynnol / mpa |
Cynnyrch Cryfder / MPA |
Elongation/% |
Caledwch Brinell / HB |
||||
|
Efydd tun |
Zcusn3zn11pb4 |
Cydbwysedd sy'n weddill |
3.0-6.0 |
2.0-4.0 |
9.0-13.0 |
Zcusn3zn11pb4 |
Castio tywod |
175 |
... |
8 |
590 |
|
Castio metel |
215 |
... |
10 |
590 |
|||||||
|
Sail |
ISO o safonau rhyngwladol |
Cyn Undeb Sofietaidd |
Unol Daleithiau (Symbol) |
Japaniaid |
Yr Almaen |
Brydain |
Ffrainc |
|
Zcusn3zn11pb4 |
... |
BPO3ц12C5 |
C84500 |
Bc1 |
... |
... |
... |
|
ZCUSN5PB5ZN5 Nodweddion:ymwrthedd gwisgo da ac ymwrthedd cyrydiad, prosesu hawdd, perfformiad castio a thyndra aer . rhannau gwrthsefyll gwisgo a gwrthsefyll cyrydiad fel bushings, bushings, leinin silindr, cydiwr piston, chwarren bwmp, chwarren bwmp, gêr llyngyr, ac ati {. |
|||||||||||
|
Enw'r Alloy |
Gradd aloi |
Prif Gyfansoddiad Cemegol/% |
Gradd aloi |
Dull castio |
Priodweddau mecanyddol, dim llai na |
||||||
|
Gopr |
Blaeni |
Tunia ’ |
Sinc |
cryfder tynnol / mpa |
Cynnyrch Cryfder / MPA |
Elongation/% |
Caledwch Brinell / HB |
||||
|
Efydd tun |
Zcusn5pb5zn5 |
Cydbwysedd sy'n weddill |
4.0-6.0 |
4.0-6.0 |
4.0-6.0 |
Zcusn5pb5zn5 |
Castio tywod, castio metel |
200 |
90 |
13 |
590 |
|
Sail |
ISO o safonau rhyngwladol |
Cyn Undeb Sofietaidd |
Unol Daleithiau (Symbol) |
Japaniaid |
Yr Almaen |
Brydain |
Ffrainc |
|
Zcusn5pb5zn5 |
Cupb5sn5zn5 |
BPO5ц5C5 |
C83600 |
Bc6 |
G-CUSN5ZNPB |
Lg2 |
Cupb5sn5zn5 |
|
Nodweddion ZCUSN10PB1:Caledwch uchel, ymwrthedd cyrydiad rhagorol, ddim yn hawdd cynhyrchu ffenomen marwolaeth brathiad, perfformiad castio da a thorri . gellir defnyddio gwrthiant gwisgo i weithio o dan lwyth uchel (o dan 20 MPa) a chyflymder llithro uchel (8 m/s) |
|||||||||||
|
Enw'r Alloy |
Gradd aloi |
Prif Gyfansoddiad Cemegol/% |
Gradd aloi |
Dull castio |
Priodweddau mecanyddol, dim llai na |
||||||
|
Gopr |
Blaeni |
Tunia ’ |
Ffosfforws |
cryfder tynnol / mpa |
Cynnyrch Cryfder / MPA |
Elongation/% |
Caledwch Brinell / HB |
||||
|
10-1 Efydd tun |
Zcusn10pb1 |
Cydbwysedd sy'n weddill |
... |
9.0-11.5 |
0.5-1.0 |
Zcusn10pb1 |
Castio tywod |
220 |
130 |
3 |
785 |
|
Castio metel |
310 |
170 |
2 |
885 |
|||||||
|
Sail |
ISO o safonau rhyngwladol |
Cyn Undeb Sofietaidd |
Unol Daleithiau (Symbol) |
Japaniaid |
Yr Almaen |
Brydain |
Ffrainc |
|
Zcusn10pb1 |
Cusn10p |
BPO10ф1 |
C90700 |
PBC2B |
... |
PB4 |
... |
|
Nodweddion ZCUSN10PB2:ymwrthedd cyrydiad da, gwrthiant gwisgo a pherfformiad torri, perfformiad castio da, crynoder uchel castiau a thyndra aer da . ffitiadau pibellau pwysig, yn ogystal â falfiau, ceiliogod, pympiau, gerau, impelwyr a gerau llyngyr, a ddefnyddir yn bennaf i weithredu ar lwythi cyfrwng ac uchel a chyflymder llithro bach |
|||||||||||
|
Enw'r Alloy |
Gradd aloi |
Prif Gyfansoddiad Cemegol/% |
Gradd aloi |
Dull castio |
Priodweddau mecanyddol, dim llai na |
||||||
|
Gopr |
Blaeni |
Tunia ’ |
Sinc |
cryfder tynnol / mpa |
Cynnyrch Cryfder / MPA |
Elongation/% |
Caledwch Brinell / HB |
||||
|
10-2 Efydd tun |
Zcusn10pb2 |
Cydbwysedd sy'n weddill |
9.0-11.0 |
1.0-3.0 |
Zcusn10pb2 |
Castio tywod |
240 |
120 |
12 |
685 |
|
|
Castio metel |
245 |
140 |
6 |
785 |
|||||||
|
Sail |
ISO o safonau rhyngwladol |
Cyn Undeb Sofietaidd |
Unol Daleithiau (Symbol) |
Japaniaid |
Yr Almaen |
Brydain |
Ffrainc |
|
Zcusn10sn2 |
Cusn10z2 |
BPO10ц2 |
C90500 |
Bc3 |
G-CUSN10ZN |
G1 |
Cusn12 |